High or low hydroxyl ion (OH) concentration 100 um/200um/300um/400um Fibers for UV-to-visible visible-to-NIR application
Technical data
Wavelength / spectralrangeUV:190 – 1200nm
WF:300 – 2400nm
Numerical aperture(NA)0,12 ± 0,02|0,22 ± 0,02|0,28 ± 0,02orcustomised
Operating temperature-190bis+350°C
Core diameter Available from 25 to 2000μm
Standard core / cladding ratios1 : 1,04|1 : 1,06|1 : 1,1|1 : 1,15|1 : 1,2|1 : 1,25|1 : 1,4 or customised
OH content UV:high(>700ppm)
WF:low(<1ppm)
Fibers with OH contents<0,25ppm are available upon request
Standard proof test100kpsi (nylon,ETFE,acrylate jacket) |70kpsi (polyimide jacket)
Minimum bending radius50 × cladding diameter(short-term mechanical stress)
150 × corediameter(during use with high laser power)
◆ Fine transmission performance at ultraviolet waveband, antiγ-ray at 800nm;
◆ Applied in ultraviolet spectrum analysis, laser transmission, health detection, nuclear energy and
semiconductor etc;
◆ NA=0.22±0.02 (0.1to 0.28 on request);
CCDR: 1:1.04, 1:1.1, 1:1.2 (1:1.06, 1:1.15, 1:1.25, 1:1.4on request)
First choice for applications including spectroscopy, medical diagnostics, medical technology, laser delivery systems and many more.
| Core[μm](±2%) | 50 | 100 | 105 | 115 | 192 | 200 | 300 | 365 | 400 | 500 | 600 | 800 | 1000 |
| cladding[μm](±2%) | 125 | 110 | 125 | 125 | 200 | 220 | 330 | 400 | 440 | 550 | 660 | 880 | 1100 |
| coating material : Acrylate, Temperature range[℃]: -40-85 | |||||||||||||
| coating[μm](±3%) | 245 | 245 | 245 | 245 | 245 | 350 | 450 | 550 | 550 | 770 | 840 | 1100 | 1300 |
| coating material : Polymide, Temperature range[℃]: -65-300 | |||||||||||||
| coating[μm](±3%) | 145 | 125 | 145 | 145 | 145 | 245 | 355 | 425 | 480 | 575 | 710 | - | - |